KARAKTERISTIK PEREKAT DAN PEREKATAN TANIN RESORSINOL FORMALDEHIDA PADA SIREKAT AKASIA (Acacia mangium) dan PULAI (Alstonia scholaris)

Adhesion and Adhesive Characteristics of Tannins Resorcinol Formaldehyde on Sirekat Acacia (Acacia mangium) and Pulai (Alstonia scholaris)

Penulis

  • Safni Auliarta Fakultas Pertanian
  • Evi Sribudiani
  • Sonia Somadona

DOI:

https://doi.org/10.24259/perennial.v17i2.12759

Kata Kunci:

Keywords: Adhesive, Adhesion, Tannin, resorcinol, Formaldehyde

Abstrak

The composition of the adhesive content of Tannin Resorcinol Formaldehyde (TRF) is considered more environmentally friendly to use when compared to the phenol resorcinol formaldehyde (RPF) adhesive. In this study to test the strength of the adhesive, acacia (Acacia mangium) and pulai (Alstonia scholaris) were used. This study aims to determine: 1. The characteristics and quality of the adhesive composition of eucalyptus bark tannins, resorcinol and formaldehyde based on SNI 6/4567/1998. 2. The strength of the gluing composition of eucalyptus bark tannins, resorcinol and formaldehyde on acacia and pulai wood syrup based on SNI 6/6049/1999. The research was conducted using a non-factorial Completely Randomized Design (CRD) consisting of 6 treatments of adhesive composition with 5 repetitions, in order to obtain 30 test samples. The data obtained from the research results were analyzed by means of variance using SPSS 20. Furthermore, if the variance results have a significant effect, further analysis will be carried out using Duncan's New Multiple Range Test (DNMRT) at the 5% level. The results of the research that has been carried out, the six different adhesive compositions produce different values ​​in each treatment, except for treatment P1. P1 has the shape and appearance of a jelly-shaped adhesive so that it cannot be tested and applied to acacia and pulai wood glue. Treatments P2 to P6 can be applied and used for testing and bonding. The pH test and gelatinization test of all treatments were included in SNI 6/4567/1998, the P2 viscosity test did not pass SNI 6/4567/1998. The shear bond strength test was carried out to determine the strength of the adhesive referring to SNI 6/6049/1999, the average value of the best wet shear adhesion test in treatment P6 was 7.89 N/mm2 and the highest average value of shear bonding strength dry on P5 treatment of 26,09 N/mm2 

Unduhan

Data unduhan belum tersedia.

Referensi

Anshari, B. 2006. Pengaruh variasi tekanan kempa terhadap kuat lentur kayu laminasi dari kayu meranti dan keruing. Civil Engineering. 8 (1): 26-27.

Arinana., Farah, D. 2009. Kualitas kayu pulai (Alstonia scholaris) terdensifikasi (sifat fisis, mekanis dan keawetan). Institut Pertanian Bogor. Jurnal Ilmu dan Teknologi Hasil Hutan. 2 (2): 81-83

Awaliyan, H.M Rahkmat., E. Rosamah dan E. Sukanto. 2017. Karakteristik tanin dari ekstrak kulit kayu leda (Eucalyptus deglupta Blume.). Jurnal Hutan Tropica. ISSN 2599 1205, eISSN 2599 1183. 1 (1): 17-20.

Budiyanto, E., Asroni, & Pranowo. A. 2016. Pengaruh temperatur cetakan dan lama pengempaan terhadap keteguhan rekat pada kayu lapis sebagai bahan baku pembuatan drum shell. Jurnal Teknik Mesin Univ. Muhammadiyah Metro TURBO p-ISSN: 2301-6663, e-ISSN: 2477-250X. 5 (2): 122-137.

Dave, N.A., Winaya, I.N.S., & Widiyarta, I.M. 2019. Studi pengaruh variasi penambahan polivinil asetat pada limbah tinta sebagai bahan baku pembuatan perekat. Jurnal Ilmiah TEKNIK DESAIN MEKANIK. 8 (4): 759.

Herlina, N., & Nurhasmawati, P. 2014. Studi Pengaruh Penambahan Resorsinol Pada Pembuatan Perekat Likuida Sabut Kelapa. Laporan Akhir Pelaksanaan Penelitian PNBP USU. Universitas Sumatera Utara.

Iskandar, M.I., Pratiwi, D.A., & Wiyantina, N.. 2017. Pengaruh hardener dan ekstender dalam perekat tanin resorsinol formaldehida terhadap emisi formaldehida kayu lapis. Jurnal ITEKIMA ISSN: 2548-947x. 2 (1): 16-19.

Istiqomah, M., & Herlina, N. 2014. Pengaruh penambahan resorsinol pada pembuatan perekat likuida sabut kelapa. Jurnal Teknik Kimia USU. 4 (2): 39.

Jannah, R. 2018. Pengaruh Jenis Perekat terhadap Nilai Kalor Briket Arang Tempurung Kawista (Limonia acidissima) Teraktivasi NaOH Skripsi (dipublikasi). Universitas Islam Negeri Maulana Malik Ibrahim. Malang.

Jasni. 2015. Keawetan alami 57 jenis kayu Indonesia dengan pengujian di bawah naungan. Jurnal Penelitian Haasil Hutan ISSN:0216 4329. 34 (3). 185.

Lestari, A.S.R.D. 2018. Sintesis dan Karakterisasi Perekat Tanin Mahoni untuk Balok Glulam dari Kayu Cepat Tumbuh, Tesis Magister, Institut Pertanian Bogor, Bogor.

Prayitno, T.A. 1996. Perekatan Kayu. Fakultas Kehutanan Universitas Gadjah Mada. Yogyakarta.

Rachmawati, O., Sugita, P., & Santoso, A. 2018. Sintesis perekat tanin resorsinol dari ekstrak kulit pohon mangiium untuk peningkatan kualitas batang sawit. Jurnal Penelitian Hasil Hutan. ISSN: 0216-4329 Terakreditasi.33-46.

Risnasari, I., & Ruhendi, S. 2006. Sifat Dasar Perekat Likuida kayu dari beberapa jenis kayu. Universitas Sumatera Utara. Medan. Peronema Forestry Science Journal. 2 (2).

Santoso, A. 2005. Pemanfaatan lignin dan tanin sebagai alternatif substitusi bahan perekat kayu komposit. in simposium nasional polimer V. ISSN 1410-8720: 155-157.

Santoso, A., Surdiding. R., Yusuf. S.H., & Suminar. S.A. 2004. Sintesis dan karakterisasi resin lignin resorsinol formaldehida sebagai perekat kayu lamina. Majalah IPTEK. 15 (3).

Santoso, A., Sulatiningsih, I.M., Gustan, P., & Jasni. 2015. Pemanfaatan ekstrak kayu merbau untuk perekat produk laminasi bambu. Jurnal Penelitian Hasil Hutan. ISSN: 0216-4329 Terakreditasi. 34 (2): 89-92.

Standar Nasional Indonesia 1994, Kuat geser kayu (SNI 03 – 3400 – 1994), Standar Nasional Indonesia, Jakarta.

Standar Nasional Indonesia 1998, Fenol formaldehida cair untuk perekat kayu lapis (SNI 06-4567-1998), Standar Nasional Indonesia, Jakarta.

Standar Nasional Indonesia 1999, Kualitas perekatan untuk perekatan kayu lapis (SNI 06-6049-1999), Standar Nasional Indonesia, Jakarta.

Sucipto, T., & Surdiding, R. 2012. Analisis kualitas kayu laminasi akasia (Akasia mangium) dengan perekat polistirena. Jurnal of Forestry ISSN 2089-9890. 1 (1): 19-24.

Susanto, H. 2013. Karakteristik Balok Laminasi (Glulam) Kayu Eukaliptus (Eucalyptus urophylla St. Blake). Skripsi. Institut Pertanian Bogor, Bogor.

##submission.downloads##

Diterbitkan

2021-10-31

Cara Mengutip

Auliarta, S., Sribudiani, E., & Somadona, S. (2021). KARAKTERISTIK PEREKAT DAN PEREKATAN TANIN RESORSINOL FORMALDEHIDA PADA SIREKAT AKASIA (Acacia mangium) dan PULAI (Alstonia scholaris): Adhesion and Adhesive Characteristics of Tannins Resorcinol Formaldehyde on Sirekat Acacia (Acacia mangium) and Pulai (Alstonia scholaris). PERENNIAL, 17(2), 35-44. https://doi.org/10.24259/perennial.v17i2.12759

Artikel paling banyak dibaca berdasarkan penulis yang sama